Sikafloor®-264 ZA
Sikafloor®-264 ZA is a 2-part epoxy coloured coating that can provide a hard wearing, seamless, low maintenance, smooth gloss finish or slip resistant finish when broadcast with different aggregate grades.
- Seamless and hygienic
- Good chemical and mechanical resistance
- Easy application
- Waterproof
- Gloss finish
- Slip resistant surface to suit clients requirements
- Can be filled with sand to produce a self-smoothing resin
- Low maintenance
Usage
- Sikafloor®-264 ZA is used as a:
- Self smoothing wearing floor coating on concrete and cementitious substrates
- Smooth wearing roller coating on concrete and cementitious screed substrates
- Slip resistant wearing coating on concrete and cementitious screeds
- Seal coat or top coat for slip-resistant broadcast systems
- Please note:
- The Product may only be used by experienced professionals.
- The Product may only be used for interior applications.
Advantages
- Seamless and hygienic
- Good chemical and mechanical resistance
- Easy application
- Waterproof
- Gloss finish
- Slip resistant surface to suit clients requirements
- Can be filled with sand to produce a self-smoothing resin
- Low maintenance
Packaging
| Part A | 10.0 Ltr (15.8kg) containers |
| Part B | 4.2 Ltr (4.2kg) containers |
| Part A+B | 14.2 Ltr (20kg)ready to mix units |
| Part A+B+C | |
| 1:1 (resin:filler SS2 (0.1 - 0.3mm)) | 21.28ltr or 40kg (20kg Part C) |
| 1:1.04 (resin:filler SS1 (0.1 - 0.3mm)) | 16.67ltr or 28kg (8kg Part C) |
Colour
| Resin - part A: | coloured, liquid |
| Hardener - part B | transparent, liquid |
RAL 1002, 7032, 7035, 7037, 7038, 7042,
Other colours on request.
Under direct sun light there may be some discolouration and colour variation; this has no influence on the function and performance of the coating.
Product Details
APPROVALS / STANDARDS
Particle emission certificate Sikafloor-264 ZA CSM Statement of Qualification – ISO 14644-1, class 4– Report No. SI 0904-480 and and GMP class A, Report No. SI 1008-533..
Outgassing emission certificate Sikafloor-264 ZA: CSM Statement of
Qualification – ISO 14644-8, class 6,5 - Report No. SI 0904-480.
Good biological Resistance in accordance with ISO 846, CSM Report No. 1008-533
Fire classification in accordance with EN 13501-1, Report-No. 2007-B-0181/16, MPA Dresden, Germany, February 2007.
ISEGA Certificate of Conformity 31964 U 11
Chemical Base
Epoxy
Shelf Life
24 months from date of production
Storage Conditions
The packaging must be stored properly in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5°C and +30°C.
Density
| Part A | ~ 1.50 kg/l |
| Part B | ~ 1.00 kg/l |
| Mixed resin | ~ 1.44 kg/l |
| Filled resin (1:1) | ~ 1.44 kg/l |
Solid content by weight
~100 %
Total solid epoxy composition acc. to the test method Deutsche Bauchemie e.V. (German Association for construction chemicals)
Solid content by volume
~100 %
Shore D Hardness
| 76 (7 days / +23°C) | (DIN 53 505) |
Abrasion Resistance
| 70 mg (CS 10/1000/1000) (8 days / +23°C) | (DIN 53 109 (Taber Abrader Test)) |
Compressive Strength
| Resin (filled 1:0,9 with QS SS2: ~ 50 N/mm2 (28 days / +23°C) | (EN 196-1) |
Tensile Strength in Flexure
| Resin (filled 1:0,9 with QS SS2): ~ 20 N/mm2 (28 days / +23°C) | (EN 196-1) |
Tensile Adhesion Strength
| > 1.5 N/mm² (failure in concrete) | (ISO 4624) |
Chemical Resistance
Resistant to many chemicals. Please ask for a detailed chemical resistance table
Thermal Resistance
| Exposure* | Dry heat |
| Permanent | +50°C |
| Short-term max. 7 d | +80°C |
| Short-term max. 12 h | +100°C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (steam cleaning etc.).
*No simultaneous chemical and mechanical exposure and only in combination with Sikafloor® systems as a broadcast system with approx. 3–4 mm thickness.
Application
Mixing Ratio
Part A : part B = 79 : 21 (by weight)
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Note: Low temperatures and high humidity conditions increase the probability of blooming.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
≤ 4 % pbw moisture content.
Test method: Sika®-Tramex meter, CM-measurement or Oven-dry-method.
No rising moisture according to ASTM (Polyethylene-sheet).
Pot Life
| Temperature | Time |
| +10 °C | ~50 minutes |
| +20 °C | ~25 minutes |
| +30 °C | ~15 minutes |
Curing Time
| Substrate temperature | Minimum | Maximum |
| +10 °C | 30 hours | 3 days |
| +20 °C | 24 hours | 2 days |
| +30 °C | 16 hours | 1 day |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
| Temperature | Foot traffic | Light traffic | Full cure |
| +10 °C | ~72 hours | ~ 6days | ~10 days |
| +20 °C | ~24 hours | ~ 4days | ~7 days |
| +30 °C | ~18 hours | ~ 2days | ~5 days |
Consumption
| Function | Consumption |
| Wearing layer (filled) | 1.6-1.9 kg/m2 per mm |
| Roller coat | 0.4–0.72 kg/m² |
| Seal coat or top coat for broadcast systems | 0.6–0.8 kg/m² |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc. For detailed info, please refer to the System data sheet Sikafloor® Multidur ES-24 and Sikafloor® Multidur EB-24
MIXING
Coatings
Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 3 minutes until a uniform mix has been achieved. To ensure thorough mixing pour materials into another container and mix again to achieve a smooth consistent mix. Over mixing must be avoided to minimise air entrainment.
Self-Smoothing Resin
Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 3 minutes until a uniform mix has been achieved. When parts A and B have been mixed, add the quartz sand and if required Extender T. Mix for a further 2 minutes until a uniform mix has been achieved. To ensure thorough mixing pour materials into another container and mix again to achieve a smooth consistent mix. Over mixing must be avoided to minimise air entrainment.
Mixing Tools
Sikafloor®-264 ZA (unfilled) must be thoroughly mixed using a low speed electric stirrer (300–400 rpm) or other suitable equipment. For the preparation of a self- smoothing resin, use a forced action mixer or rotating pan, paddle or trough type. Free fall mixers should not be used.
APPLICATION
Prior to application, confirm substrate moisture content, relative air humidity and dew point. If > 4 % pbw moisture content, Sikafloor® EpoCem® may be applied as a temporary moisture barrier (T.M.B.) system.
Primer
Ensure a continuous, pore free coat covers the substrate. If necessary, apply two priming coats. Apply Sikafloor®-161 by brush, roller or squeegee.
Preferred application is by using a squeegee and then back rolling in two directions at right angles to each other.
Levelling
Rough surfaces need to be levelled first. Therefore use e.g. Sikafloor®-161 levelling mortar (see PDS).
High Build Smooth Coating
Sikafloor®-264 ZA can be applied using a short-piled roller in two directions at right angles to each other.
Self-Smoothing Finish
Sikafloor®-264 ZA is poured and spread evenly using a suitable trowel/pin rake to the required thickness.
Spike roller immediately in two directions at right angles to each other to remove trowel marks, aid air release, ensure an even thickness and obtain required surface finish.
Slip Resistant Broadcast Coating
Apply a scratch coat to substrate and immediately broadcast with quartz sand to excess to produce an even distribution surface profile. Allow scratch coat to initially cure and remove all loose sand by vacuum equipment. Apply a final seal/top coat of Sikafloor®-264 ZA. For application onto damp substrates, refer to Sikafloor® MultiDur EB-12 ECC system data sheet for primer and levelling product changes.
Seal coat
Apply seal/top coat of Sikafloor®-264 ZA by squeegee at a consumption of 0,4–0,6 ltr/m2 to completely encapsulate the sand. Then using a short-piled roller, back roller in two directions at right angles to each other.
CLEANING OF TOOLS
Clean all tools and application equipment with Thinner C immediately after use. Hardened and/or cured material can only be removed mechanically.