Sika® Sanisil®
Silicone sealant for sanitary applications
Sika® Sanisil® is a 1-part, non-sag, silicone sealant with long term resistance to fungus and mildew.
- Good long term fungus and mildew resistance
- Very good adhesion to most non-porous substrates
- Good UV and weathering resistance
- Solvent free (acc. to TRGS 610)
- High elasticity and flexibility
Usage
- Sanitary or other sealing applications where mildew and fungus resistance is required
- Domestic kitchens
- For interior and exterior use
Advantages
- Good long term fungus and mildew resistance
- Very good adhesion to most non-porous substrates
- Good UV and weathering resistance
- Solvent free (acc. to TRGS 610)
- High elasticity and flexibility
Packaging
300 ml cartridge: 12 cartridges per box
Refer to current price list for packaging variations
Colour
Colour range to be defined by local sales organisation.
Product Details
APPROVALS / STANDARDS
- CE Marking and Declaration of Performance to EN 15651-3 - Sealants for non-structural use in joints in buildings - Sealants for sanitary
Chemical Base
Acetoxy silicone
Shelf Life
18 months from date of production
Storage Conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.
Density
~1,00 kg/l | (ISO 1183-1) |
Product Declaration
EN 1565-3: S XS1
Shore A Hardness
~20 (after 28 days) | (ISO 868) |
Tensile Strength
~1,8 N/mm2 | (ISO 8339) |
Secant Tensile Modulus
~0,35 N/mm2 at 100% elongation (+23 °C) | (ISO 8339) |
Elastic Recovery
> 90 % | (ISO 7389) |
Tear Propagation Resistance
~2,6 N/mm | (ISO 34) |
Movement Capability
±20 % | (ISO 9047) |
Service Temperature
−40 °C / +100 °C
Joint Design
The joint dimensions must be designed to suit the movement capability of the sealant. For joint widths more than 10 mm and less than 20 mm, a joint depth of 10 mm is recommended.
For larger joints, contact Sika Technical Services for additional information.
Application
Backing Material
Use closed cell, polyethylene foam backing rod.
Sag Flow
< 1 mm (20 mm profile, +23 °C) | (ISO 7390) |
Ambient Air Temperature
+5 °C min. / +40 °C max.
Substrate Temperature
+5 °C min. / +40 °C max., min. 3 °C above dew point temperature
Curing Rate
~3,0 mm/24 hours (+23 °C / 50 % r.h.) | (CQP* 049-2) |
*Sika Corporate Quality Procedure |
Skin Time
~25 min (+23 °C / 50 % r.h.) | (CQP 019-1) |
Consumption
Joint width [mm] | Joint depth [mm] | Joint length [m] per 300 ml |
10 | 10 | 3,0 |
15 | 10 | 2,0 |
20 | 10 | 1,5 |
Consumption depends on the roughness and absorbency of the substrate.
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
SUBSTRATE PREPARATION
The substrate must be sound, clean, dry and free of all contaminants such as dirt, oil, grease, old sealants and poorly bonded paint coatings which could affect adhesion of the sealant. The substrate must be of sufficient strength to resist the stresses induced by the sealant during movement.
Removal techniques such as wire brushing, grinding, grit blasting or other suitable mechanical tools can be used.
All dust, loose and friable material must be completely removed from all surfaces using suitable equipment before application of any activators, primers or sealant.
Sika® Sanisil® adheres without primers and/or activators.
For optimum adhesion, joint durability and critical, high performance applications such as joints on multi-storey buildings, highly stressed joints, extreme weather exposure or water immersion / exposure. The following priming and/or pre-treatment procedures must be followed:
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, PVC, galvanised steel, powder coated metals or glazed tiles. Slightly roughen surface with a fine abrasive pad. Clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth.
Before sealing, allow a waiting time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, clean and pre-treat using Sika® Aktivator-205 applied with a clean cloth. After a waiting time of > 15 minutes (< 6 hours). Apply Sika® Primer-3 N applied by brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours)
PVC has to be cleaned and pre-treated using Sika® Primer-215 applied with a brush. Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Glass must be cleaned with Isopropanol before application.
Porous substrates
Porous substrates must be primed using Sika® Primer-3 N applied by brush. For more details such as application and flash-off times, refer to the most recent Product Data Sheet of the respective pre-treatment product.
Before sealing, allow a waiting time of > 30 minutes (< 8 hours).
Adhesion tests on project specific substrates must be performed and procedures agreed with all parties before full project application.
For more detailed advice and instructions contact Sika Technical Services.
Note: Primers and activators are adhesion promoters and not an alternative to improve poor preparation / cleaning of the joint surface. Primers also improve the long term adhesion performance of the sealed joint.
MIXING
1-part ready to use
CLEANING OF TOOLS
Clean all tools and application equipment with Sika® Remover-208 immediately after use. Hardened material can only be removed mechanically. For cleaning skin, use Sika® Cleaning Wipes-100.