SikaCor® VEL
Conductive vinylester laminate system
SikaCor® VEL is a glass fibre reinforced, 2-pack vinylester based coating system and an inert powder:
- SikaCor® VEL primary screeding
- SikaCor® VEL laminate
- SikaCor® VEL top coat
- Wide ranging chemical resistance to acids, leaches, solvents and notably to oxidising and flammable substances
- Crack bridging
- Conductive
- Driveable
- Very fast hardening
Usage
SikaCor® VEL is suited for sealing reinforced concrete receiving vats and chambers, indoors or outdoors, or for steel tanks for the storage of aggressive liquids (e.g. concentrate acids, leaches and solvents). SikaCor® VEL is also suitable as a coating system to be driven on directly by vehicles with pneumatic tyres or with tyres of solid rubber, Vulkollan or polyamide, e.g. in electroplating works, pickling plants, and in plants where oxidising materials are manufactured, treated or used.Advantages
- Wide ranging chemical resistance to acids, leaches, solvents and notably to oxidising and flammable substances
- Crack bridging
- Conductive
- Driveable
- Very fast hardening
Packaging
SikaCor® VE (solution) | 25 kg net. |
SikaCor® VE (hardener) | 1 kg net. |
SikaCor® VEL (powder) | 25 kg net. |
Glass fibre matting (450 g/m2) | roll ~70 kg |
SikaCor® surface matting (~30 g/m2) | roll ~9 kg |
Colour
SikaCor® VE (solution conductive), darkgrey | ~RAL 7031 |
SikaCor® VE (solution), pebble grey | ~RAL 7032 |
Laminate: SikaCor® VE (solution) yellow glaze + | Yellowish transparent |
Product Details
APPROVALS / STANDARDS
-
Satisfies the requirements of the ‘principles of Construction and Inspection for the Protection of Waters‘ (Bau- und Prüfgrundsätze für den Gewässerschutz) of the DIBt (Deutsches Institut für Bautechnik - German Institute of Building Technology) and is building inspectorate approved for concrete
-
Coating based on vinylester for concrete protection according to EN 1504, DoP, with CE-mark.
Chemical Base
SikaCor® VE (solution) | Vinylester resin |
SikaCor® VE (hardener) | Org. peroxide |
SikaCor® VEL (powder) | Carbon powder |
Shelf Life
SikaCor® VE (solution) | 3 months |
SikaCor® VE (hardener) | 6 months |
SikaCor® VEL(powder) | 24 months |
Storage Conditions
In originally sealed containers in a cool and dry environment
(at max. + 20°C).
Density
SikaCor® VE (solution) |
|
SikaCor® VE (hardener) | ~1.1 g/cm3 |
SikaCor® VEL (powder) | ~0.54 g/cm3 (bulk density) |
SikaCor® VE (solution conductive) | ~1.26 g/cm3 |
SikaCor® VE (solution) RAL 7032 | ~1.34 g/cm3 |
Crack Bridging Ability
Up to max. 0.2 mm
Chemical Resistance
According to the approval of the DIBt (German Institute of Building Technology), approval number Z-59.12-69 for test groups 1, 1a, 2, 3, 3a, 3b, 4, 4a, 4b, 4c, 5, 5a, 5b, 6, 6b, 7, 7a, 7b, 8, 9, 9a, 10, 11, 12, 13, 14, 15 and 15a
Additional building inspectorate approval for the following materials:
- hydrochloric acid ≤ 37 %
- sulfuric acid ≤ 70 %
- nitric acid ≤ 65 %
- aqueos sodium hypochlorite (12 % active chlorine)
- hydrogen peroxid ≤ 30 %
- chromic acid ≤ 50 %
Note:
In particular cases a discoloration of media may occur.
Nevertheless this does not effect the chemical resistance itself.
Thermal Resistance
Dry heat up to approx. + 100°C
Damp heat depending on chemical exposure upon request
Electrical Resistance
≤ 1 x 108
Application
Layer Thickness
~3 mm
Ambient Air Temperature
Min. + 5°C, max. + 30°C
Relative Air Humidity
Max. 80 % (temperature ≥ 3 K above the dew point)
Provide good and sufficient ventilation during application!
Water, even in minimal quantities, may damage the accelerating system and avoid the hardening process of the mortar.
Please keep tools and mixers absolutely dry.
Surface temperature
Min. + 5°C, max. + 30°C
Pot Life
~30 min
Drying Time
Primary screeding:
Walkable | after 2 h at + 20°C |
Overcoatable | after 16 h at + 20°C |
Laminate:
Walkable and overcoatable | after 2 h at + 20°C |
Walkable and overcoatable | after 12 h at + 10°C |
Top Coats:
Walkable and overcoatable | after 2 h at + 20°C |
Walkable and overcoatable | after 12 h at + 10°C |
Consumption
Coating system and consumption
Primary screeding:
1.000 kg SikaCor® VE yellowish transparent (100 parts)
0.015 kg SikaCor® VE (hardener) (1.5 parts)
0.800 kg SikaCor® VEL (powder) (80 parts)
1.815 kg = 1 l final mixture
consumption: approx. 0.7 - 1.5 kg/m2
Laminate:
1.074 kg SikaCor® VE yellowish transparent (100 parts)
0.016 kg SikaCor® VE (hardener) (1.5 parts)
1.090 kg = 1 l final mixture
consumption: approx. 2.5 kg/m2
Top coat conductive (per layer):
1.200 kg SikaCor® VE (solution) (100 parts)
0.012 kg SikaCor® VE (hardener) (1 part)
1.212 kg = 1 l final mixture
consumption: approx. 0.3 kg/m2
Alternative (without DIBt approval):
Top coat non-conductive RAL 7032 (per layer):
1.300 kg SikaCor® VE (solution) RAL 7032 (100 parts)
0.013 kg SikaCor® VE (hardener) (1 part)
1.313 kg = 1 l final mixture
consumption: approx. 0.3 kg/m2
SUBSTRATE PREPARATION
Concrete:
Cleaning of the surface by shot-blasting, pressure blasting or milling (after milling shot-blasting is necessary). The surface must be dry, firm, fine gripping, free from loose and friable particles, mortar laitance, dust and other contaminations. Residual moisture content not above 4 % acc. to CM. The average value of surface tensile strength should not be below 1.5 N/mm2. When working on very dirty or highly chemically contaminated surfaces, additional adequate cleaning methods are necessary. Structures that are subject to the provisions of water resources law (Wasserhaushaltsgesetz - WHG) may only be coated by qualified coating firms possessing certificates of capability.
SURFACE PREPARATION
Steel:
Blast cleaning to Sa 2 ½ according to ISO 12944-4.
Free from dirt, oil and grease.
MIXING
Fill SikaCor® VE Lösung (solution) in a container and add SikaCor® VE Härter (hardener) at the specified mixing ratio. Stir thoroughly until a homogeneous compound is obtained. Then fill into a clean container to stir up again. Add powder according application and required mixing ratio. Mixing time should be at least 3 minutes.
APPLICATION
Troweling, laminating, rolling = undiluted
Primary screeding:
SikaCor® VEL primary screeding should be applied with smoothing trowel.
Laminate:
SikaCor® VEL binding material is first rolled onto the hardened SikaCor® VEL Primery screeding with a pile-fabric roller. Glass fibre matting (Vetrotex M 113 or Advantex M 113) with a mass per unit area of 450 g/m2 is then immediately laid on, pressed in with the roller and simultaneously saturated with SikaCor® VEL binding material.
A 2nd layer of the same glass fibre matting is laid on top of the 1st layer, thoroughly soaked, matting layer, pressed down in the same way with the roller, and saturated with SikaCor® VEL binding material.
Finally the 2nd layer of glass fibre matting is covered by a layer of surface matting (approx. 30 g/m2) pressed in with a laminating roller and rolled out ensuring that any air that has become included is completely expelled.
Top coat:
In order to discharge static electricity, conductive tapes / braids are glued on to the SikaCor® laminating layer, joined to the equipotential connection, and covered with the top coat SikaCor® VE Lösung leitfähig (solution conductive). Repeat application after 3 - 5 hours after curing of the first top coat.
Alternatively to the conductive top coat you can apply SikaCor® VE Lösung RAL 7032 (solution RAL 7032) as non-conductive top coat.
Non slip characters:
To improve the non-slip characteristic the 2nd coating may be broadcasted with carbon silicide (0.5 mm). Needed quantity is about 0.5 kg/m2.
CLEANING OF TOOLS
Acetone