Sikafloor® DecoDur EB-26 Quartz
Sikafloor® DecoDur EB-26 Quartz is a decorative epoxy coloured flooring system. It provides a hard wearing, seamless, slip resistance gloss finish.
- Good resistance to abrasion
- Good resistance to specific chemicals
- Decorative design
- Good mechanical resistance
- Seamless and hygienic
Usage
The System is used in commercial and public buildings and areas such as:- Airports
- Manufacturing facilities and workshops
- The System may only be used by experienced professionals.
- The System may only be used for interior applications.
Advantages
- Good resistance to abrasion
- Good resistance to specific chemicals
- Decorative design
- Good mechanical resistance
- Seamless and hygienic
Colour
| Iceberg: | Hiero: |
|
|
|
| Noblesse: | Amande: |
 |  |
| Framboise: | Fleur De Tilleul: |
 |  |
| Blue Jean: | Nougat: |
 |  |
| Mer Du Nord: | Bordeaux: |
 |  |
| Granit: | Peche: |
 |  |
| Dune: | Sanguine: |
 |  |
| Sable: | |
 |
Appearance
Slip resistance finish
System Details
APPROVALS / STANDARDS
-
Fire Classification Report EN 13501-1, Ghent, No. CR 22-0345-01
-
Slip resistance test DIN 51130, Roxeler, No.020076-20-11
System Structure
Sikafloor® DecoDur EB-26 Quartz (~2-3 mm)
| Layer | Product |
| 1. Primer or scratch coat | Sikafloor®-150 Sikafloor®-151 Sikafloor®-156 Sikafloor®-161 Sikafloor®-144 Sikafloor®-701 Contact Sika technical service for information on choosing the right primer for your project. |
| 2. Wearing layer | Sikafloor®-263 SL N or Sikafloor®-264 N |
| 3. Broadcast in excess | Sika® Quartz PU (0.3–0.8 mm or 0.7–1.2 mm) |
| 4. Top coat | Sikafloor®-169 |
Composition
Epoxy
Nominal thickness
2 mm to 3 mm
Abrasion Resistance
Cured 7 days at 23 °C | 2 g (H22 / 1000 g / 1000 cycles) |
Tensile Adhesion Strength
≥ 1.5 MPa | (EN 1542) |
Reaction to Fire
Class Bfl-s1 | (EN 13501-1) |
Chemical Resistance
Sikafloor®-169 provides the chemical resistance. Refer to the Product Data Sheet.
Note: The exposed aggregates can be affected through various chemicals. A surface finish of an acrylic dispersion as a protection and maintenance layer is recommended.
Skid / Slip Resistance
| R 11 | (DIN 51130) |
Application
Ambient Air Temperature
Maximum | +30 °C |
Minimum | +10 °C |
Relative Air Humidity
Maximum | 80 % r.h. |
Dew Point
Refer to the individual Product Data Sheet.
Substrate Temperature
Maximum | +30 °C |
Minimum | +10 °C |
Substrate Moisture Content
Refer to the individual Product Data Sheet.
Waiting Time / Overcoating
Decorative slip resistant epoxy quartz finish flooring system
Before applying Sikafloor®-263 SL N/-264 N on Sikafloor®-150/ -151/ -156/ -161 allow:
Substrate temperature | Minimum | Maximum |
+10 °C | ~24 hours | ~3 days |
+20 °C | ~12 hours | ~48 hours |
+30 °C | ~8 hours | ~24 hours |
Before applying Sikafloor®-169 on Sikafloor®-263 SL N/-264 N allow:
Substrate temperature | Minimum | Maximum |
+10 °C | ~30 hours | ~4 days |
+20 °C | ~24 hours | ~2 days |
+30 °C | ~16 hours | ~1 days |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10 °C | ~45 hours | ~6 days | ~10 days |
+20 °C | ~36 hours | ~4 days | ~7 days |
+30 °C | ~24 hours | ~3 days | ~5 days |
Note: Times apply when the last layer of the system has been applied. Times are affected by changing ambient conditions, particularly temperature and relative humidity.
Consumption
Layer | Product | Consumption |
Primer or scratch coat | 1 × Sikafloor®-150 Sikafloor®-151 Sikafloor®-156 Sikafloor®-161 Sikafloor®-144 Sikafloor®-701 | ~0.3 kg/m² to 0.5 kg/m² |
Wearing layer | Sikafloor®-263 SL N or Sikafloor®-264 N | ~0.8 kg/m² |
Broadcast in excess | Sika® Quartz PU (0.3–0.8 mm or 0.7–1.2 mm) | ~3.0 kg/m² to 4.0 kg/m² |
Top coat | Sikafloor®-169 | ~0.6 kg/m² to 0.9 kg/m² |
Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.