SikaTack®-30
Windshield Adhesive
SikaTack®-30 is a cold-applied windshield adhesive offering 30 minutes Minimum Drive Away Time (MDAT). It can be used all year round and is ideal for mobile or in-house applications.
- 30 min. Minimum Drive Away Time
- Tested acc. FMVSS 212
- Compatible with Black-Primerless and All Black installation process
- Compatible with all car makes thanks Sika’s all-in-one modulus technology
- Automotive OEM quality
PRODUCT BENEFITS
- 30 min. Minimum Drive Away Time
- Tested acc. FMVSS 212
- Compatible with Black-Primerless and All Black installation process
- Compatible with all car makes thanks Sika’s all-in-one modulus technology
- Automotive OEM quality
Usage
SikaTack®-30 is suitable for experienced professional users only. This product and related process information is designed for Automotive Glass Replacement. For other applications, tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.Packaging
| Unipack | 400 ml |
Product Details
| Chemical base | 1-component polyurethane | |
| Color (CQP001-1) | Black | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | 1.22 kg/l | |
| Non-sag properties | Good | |
| Application temperature | product ambient | 5 ─ 35 °C -10 ─ 35 °C |
| Skin time (CQP019-1) | 10 minutes A | |
| Open time (CQP526-1) | 5 minutes A | |
| Curing speed (CQP049-1) | See diagram 1 | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 65 | |
| Tensile strength (CQP036-1 / ISO 527) | 8 MPa | |
| Elongation at break (CQP036-1 / ISO 37) | 300 % | |
| Tear propagation resistance (CQP045-1 / ISO 34) | 10 N/mm | |
| Tensile lap-shear strength (CQP046-1 / ISO 4587) | 5 MPa | |
| Shear modulus (CQP081-1) | All-in-one | |
| Minimum Drive Away Time (cars) according FMVSS 212 (CQP511-1) | with airbag without airbag | 30 minutes B/C 30 minutes B/C |
| Insulation resistance (CQP079-2 / DIN IEC 60167) | Low conductive | |
| Shelf life | 9 months D |
| CQP = Corporate Quality Procedure | A) 23 °C / 50 % r. h. | B) 20 °C ─ 35 °C |
| C) Details about MDAT contact Sika | D) Storage below 25 °C |
CURE MECHANISM
SikaTack®-30 cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower (see diagram 1).
Diagram 1: Curing speed SikaTack®-30
CHEMICAL RESISTANCE
SikaTack®-30 is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.
Application
Surface Preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
The bond faces must be treated according Sika's Black-Primerless or All Black installation process. Further information on the application and use of Pre-treatments, can be found in the corresponding Product Data Sheet. Glass without ceramic coatings need proper UV protection.
Application
It is recommended to apply SikaTack®-30 with a powerful battery operated application gun.
Consider that the viscosity will increase at low temperature. For easy application, condition the adhesive at ambient temperature prior to use.
To ensure a uniform thickness of the bondline it is recommended to apply the adhesive in form of a triangular bead (see figure 1).
Figure 1: Recommended bead configuration
The open time is significantly shorter in hot and humid climate. The glass must always be installed within the open time. Never install a glass after the adhesive has built a skin.
Removal
Uncured SikaTack®-30 can be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.
Do not use solvents on skin!