Sikacryl® S

Sikacryl® S

Acrylic sealant for minor movement joints and crack filling

Sikacryl® S is a 1-part, acrylic joint sealant for internal minor movement joints and interior and exterior crack filling. It is non sag, has a primerless application, good adhesion to most construction materials, remains elastic over a wide range of temperatures and is over-paintable. Movement capability ±7.5 %.

  • Low VOC emissions
  • Good application properties
  • Good adhesion to many different substrates
  • Movement capability ±7.5 %
  • Over-paintable
Product Data Sheet Safety Data Sheet Show all documents

Usage

Sealing joints for:
  • Interior joints on many types of substrate with a limited amount of movement
  • Connections around window and door frames
  • Around wall and ceiling penetrations
Crack filling:
  • Internal and external cracks not exposed to permanent water immersion
 

Advantages

  • Low VOC emissions
  • Good application properties
  • Good adhesion to many different substrates
  • Movement capability ±7.5 %
  • Over-paintable

Packaging

300 ml cartridge: 12 cartridges per box.

Refer to current price list for packaging variations.

Colour

White, grey.

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED v2009 IEQc 4.1: Low-Emitting Materials - Adhesives and Sealants

APPROVALS / STANDARDS

  • CE Marking and Declaration of Performance to EN 15651-1 - Sealants for non-structural use in joints in buildings - Facade elements
Product Information

Chemical Base

1- part acrylic

Shelf Life

 24 months from the date of production

Storage Conditions

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.

 

Density

~1,65 kg/l

(ISO 1183-1)
System information

Compatibility

Concrete, aerated concrete, plaster, fibre cement, brick, plasterboard, aluminium, UPVC, wood
Technical Information

Shore A Hardness

~22 (28 days, +23 °C / 50 % r.h.)

(ISO 868)

Movement Capability

±7,5 %

(ISO 9046)

Service Temperature

Between -25 °C and +70 °C (dry)

Application

Application Information

Sag Flow

< 1mm (23 °C)

(ISO 7390)

Ambient Air Temperature

+5 °C min. / +35 °C max. min. +3 °C above dew point temperature

Substrate Temperature

+5 °C min. / +30 °C max.

Curing Rate

~2 mm/24 hours (+23 °C / 50 % r.h.)

(CQP* 049-2)

*  Sika Corporate Quality Procedure

Skin Time

~20 minutes (+23 °C / 50 % r.h.)

(CQP 019-1)
Consumption

Consumption

Joint length

m per (300 ml)

Joint width

mm

Joint depth

mm

3,0

10

10

2,0

15

10

Triangular joints (where the sides of the joint meet at a right angles) must have sides for bonding ≥7 mm.

Consumption calculation formula

Length of joint [m] = 300 or 600 ml / (Joint width [mm] × Joint depth [mm]) Litres / Metre run of joint = (joint width [mm]× joint depth [mm]) / 1000 [m × mm2 / l]
Application steps

SUBSTRATE PREPARATION

The substrate must be clean, dry, sound and free from oils, grease, dust and loose or friable particles. Sikacryl® S adheres without primers and/or activators. For porous substrates, e.g. concrete, plaster and / or wood, Sikacryl® S can be dissolved in water (1:1 to 1:5 ratio) and used as a primer if necessary. On plastics and paints, adhesion tests must be carried out prior to application. Iron and steel must be protected with an anti-corrosion primer.

MIXING

1-part ready to use

CLEANING OF TOOLS

Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.

 